ZG35CR24NI7SIN Ekirungo ky’eddagala kiri: C: 0.30~0.40, SI: 1.30~2.00, MN: 0.80~1.50, S: 0.03, P: 0.04, CR: 23-25.5, NI: 7.0000~8.50.50.50.50.50.50.50, n’
ZG35Cr24Ni7SiN Products are: quenching furnace, well furnace, bell cover furnace, degenerative furnace, box furnace bottom plate, annealing box, heat treatment material basket, heat resistant steel plate, hanging basket, material frame, furnace chassis, output shaft frame, well furnace hanger, heat treatment furnace blade, impeller, vacuum furnace material plate, vacuum heat treatment Ekisero ky'ebintu eby'ekikoomi .
ZG35CR24NI7SIN Omutindo: GB 8492-87 Ebifaananyi n’obuwanvu bw’okukozesa: Ebbugumu erisinga okukozesebwa liri 1100℃, amaanyi g’ebbugumu eringi, okuziyiza okw’okwokya obulungi.
ZG35CR24NI7NI7SIN Enkola y’okulongoosa, enkola erimu ekyuma ekisaanuuse eky’ekyuma ekipakisa eky’amasannyalaze arc ekikoomi ku ntandikwa y’ekipapula okulongoosa + package okufuuwa omukka gwa ammonia, okukozesa eby’obugagga ebigagga ne ggaasi ya ammonia eya layisi ng’ebintu ebisookerwako, okuyita mu kyuma ekifuuwa ammonia alloying, kiyinza okukendeeza ennyo ku nsaasaanya y’okukola kwa ammonia, okuyita mu nkola ensaamusa ebyuma.
ZG35Cr24Ni7SiN The lower limit of nickel component 7.00% and the lower limit of chromium composition 23.00% calculate the amount of nickel and chromium respectively, Add nickel plate and ferrochrome and ferrochrome nitrogen (add ferrochromium nitrogen at 0.3%), And add ferrochromium and ferronitride, Before adding iron nitride, the nitrogen at the bottom shall be replaced in Advance, nitrogen gas pressure ya 2.5~3.5kg, flow rate, okuva ku 45 okutuuka ku 65 l/min, ferrochrome erina okugattibwa mu bitundu bisatu okutuuka ku bina, kakasa nti ferrochrome esooka esaanuuka ddala nga tennagatta batch esembayo, oluvannyuma lw’okutuuka ku 70%, okugezesa okujjuvu;
ZG35Cr24Ni7SiN The smelting of nitrogen-containing high-alloy heat-resistant steel casting in the past was the smelting of electric arc furnace smelting, smelting, oxidation, reduction three stages, The smelting method has the following defects: (1), nitrogen alloying is generally in the smelting period of adding hydrogenation alloy (such as nayitrojeni ekyuma, nitric iron nitride) okutuuka ku nayitrojeni ekyuma, manganese nitride general impurity content is high, polluted steel liquid; (2) Olw’amakungula amatono aga nayitrojeni nga aloy eya haidrojeni ya bbeeyi, omuwendo gw’okusaanuusa aloy guli waggulu nnyo; (3) ekirungo kya kemiko kizibu okufuga, kyangu okuleeta kaboni, nayitrojeni n’ebitundu ebirala ebweru wa layini; (4) Okwetaaga okunene okwa chromium alloy n’omuwendo gw’okuzzaawo ogutali munywevu kyangu okuleeta kasasiro; (5). (6) Obugumu bw’amazzi amangi obw’ekyuma ekisaanuuse, si kyangu kuyiwa.